Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 12
Page 7
... weld ( Figure 2 ) . Accelerated laboratory tests on as - welded samples confirmed the better corrosion resistance of G - 30 alloy , when compared to that of alloy G in the as - welded condition ( Figure 3 ) . The effect of welding on ...
... weld ( Figure 2 ) . Accelerated laboratory tests on as - welded samples confirmed the better corrosion resistance of G - 30 alloy , when compared to that of alloy G in the as - welded condition ( Figure 3 ) . The effect of welding on ...
Page 9
... welded sheet samples of selected alloys may be tested . Unwelded samples are one - inch square with a 120 - grit ground finish . The welded samples are two inches by one inch and the surfaces are vapor blasted . Duplicate samples are ...
... welded sheet samples of selected alloys may be tested . Unwelded samples are one - inch square with a 120 - grit ground finish . The welded samples are two inches by one inch and the surfaces are vapor blasted . Duplicate samples are ...
Page 203
... welds , to avoid the occurrence of corrosion at welds , is emphasized and illustrated in many sections of the book . The subject " welding " appears in the Subject Index and is dealt with no less than 30 times ! The book is well ...
... welds , to avoid the occurrence of corrosion at welds , is emphasized and illustrated in many sections of the book . The subject " welding " appears in the Subject Index and is dealt with no less than 30 times ! The book is well ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium