Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 13
Page 219
... Vanadium Pentoxide Vanadium pentoxide which deposits continuously on the surface of the metal increases the rate of reaction linearly . Based on this conclusion , a method for the determination of corrosion was developed . 5.3 ...
... Vanadium Pentoxide Vanadium pentoxide which deposits continuously on the surface of the metal increases the rate of reaction linearly . Based on this conclusion , a method for the determination of corrosion was developed . 5.3 ...
Page 221
... vanadium pentoxide with specimens kept in vanadium pentoxide vapor and observed that more severe corrosion and erosion occurred in those immersed in the molten salts . Evans and others demonstrated that accelerated oxidation started at ...
... vanadium pentoxide with specimens kept in vanadium pentoxide vapor and observed that more severe corrosion and erosion occurred in those immersed in the molten salts . Evans and others demonstrated that accelerated oxidation started at ...
Page 222
... vanadium such as vanadium trioxide and vanadium tetraoxide , with a melting point of about 1200 C. As a result no molten salts are formed . Fig . 6 shows the correlation between the quantity of air and the type and quantity of oxides of ...
... vanadium such as vanadium trioxide and vanadium tetraoxide , with a melting point of about 1200 C. As a result no molten salts are formed . Fig . 6 shows the correlation between the quantity of air and the type and quantity of oxides of ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium