Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 47
Page 114
... sulphides . This product corresponds to mackinawite , an iron - rich iron sulphide , ' that forms a poorly protective layer on the metal surface . This compound can be later transformed into more stable iron sulphides either by chemical ...
... sulphides . This product corresponds to mackinawite , an iron - rich iron sulphide , ' that forms a poorly protective layer on the metal surface . This compound can be later transformed into more stable iron sulphides either by chemical ...
Page 117
... sulphides on the corrosion behavior of iron . The authors found that oxidation of mixed sulphate - sulphide solutions readily produces an environment that is able to pit AISI 304 stainless steel , even in the absence of chloride ions ...
... sulphides on the corrosion behavior of iron . The authors found that oxidation of mixed sulphate - sulphide solutions readily produces an environment that is able to pit AISI 304 stainless steel , even in the absence of chloride ions ...
Page 334
... sulphide , and mainly iron oxide . These films act as a physical barrier and impart a certain degree of protection to the steel surface . Biological microorganisms abound in the Dead Sea Basin brackish water ( B ) ; therefore the ...
... sulphide , and mainly iron oxide . These films act as a physical barrier and impart a certain degree of protection to the steel surface . Biological microorganisms abound in the Dead Sea Basin brackish water ( B ) ; therefore the ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium