Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 61
Page 106
... sulphate reducing reaction would increase the cathodic reaction rate indirectly . However , the direct uptake of adsorbed atomic hydrogen by bacteria is ... Sulphate - reducing Bacteria and Sulphate-Reducing Bacteria and Anaerobic Corrosion.
... sulphate reducing reaction would increase the cathodic reaction rate indirectly . However , the direct uptake of adsorbed atomic hydrogen by bacteria is ... Sulphate - reducing Bacteria and Sulphate-Reducing Bacteria and Anaerobic Corrosion.
Page 129
... sulphate - reducing bacteria . Transactions of the Faraday Society , 56 , pp . 1689-96 . Booth , G. H. , Shinn , P. M. and Wakerley , D. S. ( 1965 ) . The influence of various strains of actively growing sulphate - reducing bacteria on ...
... sulphate - reducing bacteria . Transactions of the Faraday Society , 56 , pp . 1689-96 . Booth , G. H. , Shinn , P. M. and Wakerley , D. S. ( 1965 ) . The influence of various strains of actively growing sulphate - reducing bacteria on ...
Page 163
... SULPHATE -4.0 -3.0 -2.0 -1.0 LOGO CONCN . OF AGGRESSIVE ION , MOLAR Fig . 5 : Tolerance of potassium chromate towards aggressive ions . sulphate , chloride or nitrate , abraded mild steel , 100 day test at 25 ° C ( Reference 7 ) . 2.6 ...
... SULPHATE -4.0 -3.0 -2.0 -1.0 LOGO CONCN . OF AGGRESSIVE ION , MOLAR Fig . 5 : Tolerance of potassium chromate towards aggressive ions . sulphate , chloride or nitrate , abraded mild steel , 100 day test at 25 ° C ( Reference 7 ) . 2.6 ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium