Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 65
Page 46
... steel by mechanisms previously discussed . The degree to which bacterial oxygen utilization contributes to crevice corrosion of stainless steel has been measured by Dexter and colleagues 219 218 Another case described by Tatnall reveals ...
... steel by mechanisms previously discussed . The degree to which bacterial oxygen utilization contributes to crevice corrosion of stainless steel has been measured by Dexter and colleagues 219 218 Another case described by Tatnall reveals ...
Page 57
... stainless steel , was undertaken by Little 285,286 Seawater pumped through the exchangers caused a rapid development of biofouling and corrosion of copper - nickel and aluminum surfaces and lastly , on the titanium and stainless steel ...
... stainless steel , was undertaken by Little 285,286 Seawater pumped through the exchangers caused a rapid development of biofouling and corrosion of copper - nickel and aluminum surfaces and lastly , on the titanium and stainless steel ...
Page 339
... stainless steels for fabrication of slotted or holed screens , was discussed . Corrosion products and deposits plug carbon steel ... stainless steel for these components should reduce the problem . For instance , stainless steel 316 L ...
... stainless steels for fabrication of slotted or holed screens , was discussed . Corrosion products and deposits plug carbon steel ... stainless steel for these components should reduce the problem . For instance , stainless steel 316 L ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum anaerobic Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing values vanadium