In addition , we investigated changes in the size , shape and structure of a laser affected region resulting from changes in various parameters and conditions of laser treatment such as laser beam power , beam travel velocity ...
In addition , we investigated changes in the size , shape and structure of a laser affected region resulting from changes in various parameters and conditions of laser treatment such as laser beam power , beam travel velocity ...
Page 284
With increasing Cr content both the critical current density for passivation and current density within the passive region decrease . ( In this medium 1018 steel undergoes metal dissolution at all anodic potentials . ) ...
With increasing Cr content both the critical current density for passivation and current density within the passive region decrease . ( In this medium 1018 steel undergoes metal dissolution at all anodic potentials . ) ...
Page 332
The laser affected region produced by an isolated laser beam pass consists of a melt zone surrounded by an ... has a distinct duplex structure corresponding to former pearlite and ferrite regions of the initial specimen structure .
The laser affected region produced by an isolated laser beam pass consists of a melt zone surrounded by an ... has a distinct duplex structure corresponding to former pearlite and ferrite regions of the initial specimen structure .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium