Page 70
It determined by DeSchiapparelli and DeMeybaum 356 , 357 that the pitting corrosion of aluminum aircraft components was dependent upon the anionic concentration of various organic acids , such as citric , isocitric , ketoglutaric and ...
It determined by DeSchiapparelli and DeMeybaum 356 , 357 that the pitting corrosion of aluminum aircraft components was dependent upon the anionic concentration of various organic acids , such as citric , isocitric , ketoglutaric and ...
Page 117
In the presence of either thiocyanate or thiosulphate anlons , Iron pitting takes place through sulphide formation , which reacts at the electrode surface yielding poorly protective mackinawite film . The general effect of these anions ...
In the presence of either thiocyanate or thiosulphate anlons , Iron pitting takes place through sulphide formation , which reacts at the electrode surface yielding poorly protective mackinawite film . The general effect of these anions ...
Page 41
The propensity for localized attack in the form of pitting or crevice corrosion is deduced from the relative positions of the corrosion potential ( Escorp ) , the pitting potential ( Epic ) , and the socalled protection potential ...
The propensity for localized attack in the form of pitting or crevice corrosion is deduced from the relative positions of the corrosion potential ( Escorp ) , the pitting potential ( Epic ) , and the socalled protection potential ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CORROSION REVIEWS | 3 |
BIOCORROSION IN WATER | 31 |
SulphateReducing Bacteria and Anaerobic Corrosion | 104 |
Copyright | |
53 other sections not shown
Other editions - View all
Common terms and phrases
acid activity addition alloy anaerobic anodic applied areas Association ASTM attack bacteria behaviour biological brackish carbon steel cathodic cause chemical chloride coating composition concentration containing copper corrosion products corrosion rate Dead Sea decrease deposits Desulfovibrio determined developed dissolved effect electrochemical Engineers environment et al field Figure flow formation formed fouling fuel hydrogen important increase indicate industrial inhibitor International iron laboratory layer levels lower Marine materials measurements mechanism metal metal surface methods microbial microorganisms mild steel natural observed obtained occurs organisms oxide oxygen pipelines pipes pitting plant polarization potential present problem properties protective reaction reduce resistance Saline Waters salts samples scaling seawater shown shows soil solution species stainless steel steel structures sulfate-reducing bacteria sulfide sulphide sulphur surface Table techniques temperature tests tubing values various Videla