Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 75
Page 11
... pipes may break at these areas of graphitization , if subjected to high internal pressure 35. The use of ductile iron pipes , anticipated to be 36 . corrosion - resistant , as opposed to grey iron water pipes , buried in soil , has met ...
... pipes may break at these areas of graphitization , if subjected to high internal pressure 35. The use of ductile iron pipes , anticipated to be 36 . corrosion - resistant , as opposed to grey iron water pipes , buried in soil , has met ...
Page 338
... pipes were found on the ground along the water pipelines in the Sdom area . In these AC pipes , which were partially filled with flowing water when in use , H2S accumulates in the upper empty part of the wet pipe , forming an acidic ...
... pipes were found on the ground along the water pipelines in the Sdom area . In these AC pipes , which were partially filled with flowing water when in use , H2S accumulates in the upper empty part of the wet pipe , forming an acidic ...
Page 341
... pipes when they are partially filled with flowing water due to the terrain topography allowing the accumulation of ... pipes should be used in pipeline spans , with water running in full pipe , and provided with internal and external ...
... pipes when they are partially filled with flowing water due to the terrain topography allowing the accumulation of ... pipes should be used in pipeline spans , with water running in full pipe , and provided with internal and external ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium