Page 284
... passivation and current density within the passive region decrease . ( In this medium 1018 steel undergoes metal dissolution at all anodic potentials . ) In / 18,19 / surface layers alloyed with Cr and Ni were prepared by CW - CO ...
... passivation and current density within the passive region decrease . ( In this medium 1018 steel undergoes metal dissolution at all anodic potentials . ) In / 18,19 / surface layers alloyed with Cr and Ni were prepared by CW - CO ...
Page 317
... passivation region when tested in 0.1N NaCl solution , the appearance of the specimens after the test differ significantly ( Fig . 27 ) . The surface of the 1045 steel specimen in as - received condition is strongly and 2.500 1.500 ...
... passivation region when tested in 0.1N NaCl solution , the appearance of the specimens after the test differ significantly ( Fig . 27 ) . The surface of the 1045 steel specimen in as - received condition is strongly and 2.500 1.500 ...
Page 326
... passivation effect in laser treated specimens . As can be seen in Fig . 37 , three tested specimens which were treated under similar conditions and had approximately the same content of alloying elements in the surface layer behaved ...
... passivation effect in laser treated specimens . As can be seen in Fig . 37 , three tested specimens which were treated under similar conditions and had approximately the same content of alloying elements in the surface layer behaved ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium