Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 39
Page 264
... paint coat . Fig . 6 shows that permeability to the corrosion agents permitted the development of the patina under the paint as in Fig . 5 , though it is only partially preserved . This behaviour is appreciated due to the passivating ...
... paint coat . Fig . 6 shows that permeability to the corrosion agents permitted the development of the patina under the paint as in Fig . 5 , though it is only partially preserved . This behaviour is appreciated due to the passivating ...
Page 337
... Paints ....... 6. Packing of Zinc - Ethyl Silicate Paints ............... 7. Application of Zinc - Ethyl Silicate Paints 8. Zinc - Ethyl Silicate Paint Testing Page .......... 338 338 .................. 338 339 340 340 341 ...
... Paints ....... 6. Packing of Zinc - Ethyl Silicate Paints ............... 7. Application of Zinc - Ethyl Silicate Paints 8. Zinc - Ethyl Silicate Paint Testing Page .......... 338 338 .................. 338 339 340 340 341 ...
Page 344
... paints with the same zinc content in the dry film have different PVC values ; the epoxy paint will show the lower value . This would imply that for ethyl silicate paints the binder volume necessary to agglutinate the same number of zinc ...
... paints with the same zinc content in the dry film have different PVC values ; the epoxy paint will show the lower value . This would imply that for ethyl silicate paints the binder volume necessary to agglutinate the same number of zinc ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium