... organisms , contributing to the variable oxygen concentration with depth . Macroorganisms attach to metal structures in the sea and hence , create a discontinuous oxygen - deficient area under their base which encourages corrosion ...
... organisms , contributing to the variable oxygen concentration with depth . Macroorganisms attach to metal structures in the sea and hence , create a discontinuous oxygen - deficient area under their base which encourages corrosion ...
Page 40
... organism , especially dead organisms , and the metal , results in differential aeration of the metal surface . Correspondingly , when the metal is dependent upon oxygen - induced passivity for corrosion resistance , the co - existence ...
... organism , especially dead organisms , and the metal , results in differential aeration of the metal surface . Correspondingly , when the metal is dependent upon oxygen - induced passivity for corrosion resistance , the co - existence ...
Page 44
... organisms . aluminum , copper and brass appeared to be retarded possibly because of a crust of non - biogenic corrosion product on the metal . As well , a study of fouling on metal structures of North Sea platforms revealed the presence ...
... organisms . aluminum , copper and brass appeared to be retarded possibly because of a crust of non - biogenic corrosion product on the metal . As well , a study of fouling on metal structures of North Sea platforms revealed the presence ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum anaerobic Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing values vanadium