Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 66
Page 268
... method , a corrosion current method and a polarisation resistance method . In general there was good agreement between the results from these three methods . The comparison would however be more valid if the calibration curves had been ...
... method , a corrosion current method and a polarisation resistance method . In general there was good agreement between the results from these three methods . The comparison would however be more valid if the calibration curves had been ...
Page 269
... method and the anodic method ( Table V ) . Of the three the chemical dissolution method was considered the least accurate . The cathodic method was in fair agreement with the anodic method ( Figure 21 ) . Of the two the anodic method ...
... method and the anodic method ( Table V ) . Of the three the chemical dissolution method was considered the least accurate . The cathodic method was in fair agreement with the anodic method ( Figure 21 ) . Of the two the anodic method ...
Page 270
... methods / 56 / . Chemical Dissolution Method Porosity Test Method Used Polarisation Resistance Method Cathodic Corrosion Current Methods % Exposed Steel % Exposed Steel % Exposed Steel 0.36 0.29 0.51 0.4 0.22 0.21 0.25 0.075 0.09 0.15 ...
... methods / 56 / . Chemical Dissolution Method Porosity Test Method Used Polarisation Resistance Method Cathodic Corrosion Current Methods % Exposed Steel % Exposed Steel % Exposed Steel 0.36 0.29 0.51 0.4 0.22 0.21 0.25 0.075 0.09 0.15 ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium