Page 171
... indicate the periods in which contamination peaks occur , and may indicate need for dosage alterations . Condensate in Sugar and Alcohol Plants pH Monitoring . pH. Fig . 3 : Coupons position in the body of the evaporator . Fig . 4 ...
... indicate the periods in which contamination peaks occur , and may indicate need for dosage alterations . Condensate in Sugar and Alcohol Plants pH Monitoring . pH. Fig . 3 : Coupons position in the body of the evaporator . Fig . 4 ...
Page 173
... indicate actual intensity of the corrosion process ; a great part of the ferric oxide formed may deposit inside the equipment , and displacements of such corrosion product deposits may happen periodically . 3. The instantaneous ...
... indicate actual intensity of the corrosion process ; a great part of the ferric oxide formed may deposit inside the equipment , and displacements of such corrosion product deposits may happen periodically . 3. The instantaneous ...
Page 337
... indicate an active behaviour of the carbon steel in the saline waters as shown in Figure 12. Large anodic currents ... indicates that the corrosion in the neutral saline water is controlled by the reduction of dissolved oxygen . The ...
... indicate an active behaviour of the carbon steel in the saline waters as shown in Figure 12. Large anodic currents ... indicates that the corrosion in the neutral saline water is controlled by the reduction of dissolved oxygen . The ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium