... hydrogen , causing depolarization , metal dissolution and pitting 90 . as a The fact that iron sulfides have been shown to be cathodic to iron raises other possibilities . Accordingly , bacteria on the surface of the ferrous sulfide may ...
... hydrogen , causing depolarization , metal dissolution and pitting 90 . as a The fact that iron sulfides have been shown to be cathodic to iron raises other possibilities . Accordingly , bacteria on the surface of the ferrous sulfide may ...
Page 50
... hydrogen sulfide , taken to be indicative of the corrosive activities of sulfate - reducers . Bacterially - generated hydrogen sulfide also is commonly implicated in the corrosion of sewage components 244 . 245 Ulanovskii and Ledenev ...
... hydrogen sulfide , taken to be indicative of the corrosive activities of sulfate - reducers . Bacterially - generated hydrogen sulfide also is commonly implicated in the corrosion of sewage components 244 . 245 Ulanovskii and Ledenev ...
Page 60
... Hydrogen sulfide vapor released from polluted water in desalination plants further aggravates corrosion of copper heat exchanger tubes . Apparently , little hydrogen sulfide is required to accelerate corrosion of copper alloys . It is ...
... Hydrogen sulfide vapor released from polluted water in desalination plants further aggravates corrosion of copper heat exchanger tubes . Apparently , little hydrogen sulfide is required to accelerate corrosion of copper alloys . It is ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium