Rather , Schaschl observed that elemental sulfur mimics dissolved oxygen in causing corrosion of steel . The solubility of sulfur is integral to its corrosive activity . Sulfur is solubilized by sulfide ions , the solubility also ...
Rather , Schaschl observed that elemental sulfur mimics dissolved oxygen in causing corrosion of steel . The solubility of sulfur is integral to its corrosive activity . Sulfur is solubilized by sulfide ions , the solubility also ...
Page 221
According to Logan , the reaction is : 14 V205 + 20 NaVO3 + 2 ( 5 Na2O , V204 , 11 V205 ) + O2 C. Dissolution of oxygen ... The reaction may be : Metal + mixture with high dissolved oxygen content → Oxide + mixture with low dissolved ...
According to Logan , the reaction is : 14 V205 + 20 NaVO3 + 2 ( 5 Na2O , V204 , 11 V205 ) + O2 C. Dissolution of oxygen ... The reaction may be : Metal + mixture with high dissolved oxygen content → Oxide + mixture with low dissolved ...
Page 298
Saline waters contain a high concentration of dissolved , ionized mineral salts mainly chlorides and sulphates , which are aggressive ions in the context of corrosion . Their amounts , relative to carbonates and bicarbonates , are of ...
Saline waters contain a high concentration of dissolved , ionized mineral salts mainly chlorides and sulphates , which are aggressive ions in the context of corrosion . Their amounts , relative to carbonates and bicarbonates , are of ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CORROSION REVIEWS | 3 |
BIOCORROSION IN WATER | 31 |
SulphateReducing Bacteria and Anaerobic Corrosion | 104 |
Copyright | |
53 other sections not shown
Other editions - View all
Common terms and phrases
acid activity addition alloy anaerobic anodic applied areas Association ASTM attack bacteria behaviour biological brackish carbon steel cathodic cause chemical chloride coating composition concentration containing copper corrosion products corrosion rate Dead Sea decrease deposits Desulfovibrio determined developed dissolved effect electrochemical Engineers environment et al field Figure flow formation formed fouling fuel hydrogen important increase indicate industrial inhibitor International iron laboratory layer levels lower Marine materials measurements mechanism metal metal surface methods microbial microorganisms mild steel natural observed obtained occurs organisms oxide oxygen pipelines pipes pitting plant polarization potential present problem properties protective reaction reduce resistance Saline Waters salts samples scaling seawater shown shows soil solution species stainless steel steel structures sulfate-reducing bacteria sulfide sulphide sulphur surface Table techniques temperature tests tubing values various Videla