Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 38
Page 283
... ( curve a ) ; -0.14 V ( curve b ) ; -0.12 V ( curve c ; -0.09 V ( curve d ) . Samples held at -0.12 V showed small spheres buried in a thin layer of corrosion products / 5 / . Open circuit vs. time records obtained by means of " in situ ...
... ( curve a ) ; -0.14 V ( curve b ) ; -0.12 V ( curve c ; -0.09 V ( curve d ) . Samples held at -0.12 V showed small spheres buried in a thin layer of corrosion products / 5 / . Open circuit vs. time records obtained by means of " in situ ...
Page 358
... curve is obtained by adopting either the potentiostatic or the galvanostatic configuration and choosing the most appropriate type of excitation from static , dynamic or pulse . In the case of the static method , the experimental curve ...
... curve is obtained by adopting either the potentiostatic or the galvanostatic configuration and choosing the most appropriate type of excitation from static , dynamic or pulse . In the case of the static method , the experimental curve ...
Page 152
... curve Z = -Z ( Z ) and by Z , axis allows an accurate discrimination of the three electrochemical behaviours to be obtained . The mean corrosion rates , at increasing flow rates , are 0.772 mg ( cm2h ) 1 , 0.677 mg ( cm2h ) 1 and 0.664 ...
... curve Z = -Z ( Z ) and by Z , axis allows an accurate discrimination of the three electrochemical behaviours to be obtained . The mean corrosion rates , at increasing flow rates , are 0.772 mg ( cm2h ) 1 , 0.677 mg ( cm2h ) 1 and 0.664 ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium