Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 58
Page 46
... components in a paper mill , where the circulating water was rich in sulfur compounds . Corroded areas displayed an accumulation of aerobic slime , including Pseudomonas , Aerobacter , Flavobacterium and Bacillus . Underneath were ...
... components in a paper mill , where the circulating water was rich in sulfur compounds . Corroded areas displayed an accumulation of aerobic slime , including Pseudomonas , Aerobacter , Flavobacterium and Bacillus . Underneath were ...
Page 59
... components fouled less quickly and supported a less heterogenous bacterial population than aluminum components of a heat exchanger immersed in seawater . over corrosion Sulfide films which develop over metal structures in polluted ...
... components fouled less quickly and supported a less heterogenous bacterial population than aluminum components of a heat exchanger immersed in seawater . over corrosion Sulfide films which develop over metal structures in polluted ...
Page 338
... components of the asbestos - cement pipe occurs , resulting in significant loss of wall - thickness and , consequently , loss of strength properties , sometimes with the formation of cracks and even holes . These upper portions of the ...
... components of the asbestos - cement pipe occurs , resulting in significant loss of wall - thickness and , consequently , loss of strength properties , sometimes with the formation of cracks and even holes . These upper portions of the ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium