Page 25
Iron sulfide is known to 42 depolarize cathodic steel in bacteria - free systems Iron sulfides , formed by the reaction of biogenic sulfide ions with ferrous ions which arise at the anodes , may be deposited protective film on the metal ...
Iron sulfide is known to 42 depolarize cathodic steel in bacteria - free systems Iron sulfides , formed by the reaction of biogenic sulfide ions with ferrous ions which arise at the anodes , may be deposited protective film on the metal ...
Page 109
Experimental results were interpreted as a confirmation of the cathodic activity of bacteria ( Figure 4 ) . However , corrosion rates obtained in the laboratory were substantially lower than those measured in the field .
Experimental results were interpreted as a confirmation of the cathodic activity of bacteria ( Figure 4 ) . However , corrosion rates obtained in the laboratory were substantially lower than those measured in the field .
Page 110
During the 70's Costello ( 1974 ) assumed that the bacterial action on corrosion Indirect through the effect of HS on the cathodic reaction . It was concluded that has could be used as an alternative cathodic reactant at neutral pH ...
During the 70's Costello ( 1974 ) assumed that the bacterial action on corrosion Indirect through the effect of HS on the cathodic reaction . It was concluded that has could be used as an alternative cathodic reactant at neutral pH ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CORROSION REVIEWS | 3 |
BIOCORROSION IN WATER | 31 |
SulphateReducing Bacteria and Anaerobic Corrosion | 104 |
Copyright | |
53 other sections not shown
Other editions - View all
Common terms and phrases
acid activity addition alloy anaerobic anodic applied areas Association ASTM attack bacteria behaviour biological brackish carbon steel cathodic cause chemical chloride coating composition concentration containing copper corrosion products corrosion rate Dead Sea decrease deposits Desulfovibrio determined developed dissolved effect electrochemical Engineers environment et al field Figure flow formation formed fouling fuel hydrogen important increase indicate industrial inhibitor International iron laboratory layer levels lower Marine materials measurements mechanism metal metal surface methods microbial microorganisms mild steel natural observed obtained occurs organisms oxide oxygen pipelines pipes pitting plant polarization potential present problem properties protective reaction reduce resistance Saline Waters salts samples scaling seawater shown shows soil solution species stainless steel steel structures sulfate-reducing bacteria sulfide sulphide sulphur surface Table techniques temperature tests tubing values various Videla