Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 78
Page 227
... carbon steel A216-53T WCB 0.35 C max Usual Maximum Service , Temp . F 850 Cast carbon steel A216-53T WCA 0.25 C max 850 Forged carbon steel A105-55T 1 & 11 0.35 C max 850 Cast chromium - molybdenum steel A217-55 WC6 0.20 C max , 1.25 Cr ...
... carbon steel A216-53T WCB 0.35 C max Usual Maximum Service , Temp . F 850 Cast carbon steel A216-53T WCA 0.25 C max 850 Forged carbon steel A105-55T 1 & 11 0.35 C max 850 Cast chromium - molybdenum steel A217-55 WC6 0.20 C max , 1.25 Cr ...
Page 228
Seamless carbon steel pipe Seamless carbon steel pipe Seamless carbon steel pipe Carbon - molybdenum steel pipe Boiler and superheater tubes 0.06 to 0.18 C , 0.25 Si max. ASTM Pertinent Nominal Common Name Designation Grade Composition ...
Seamless carbon steel pipe Seamless carbon steel pipe Seamless carbon steel pipe Carbon - molybdenum steel pipe Boiler and superheater tubes 0.06 to 0.18 C , 0.25 Si max. ASTM Pertinent Nominal Common Name Designation Grade Composition ...
Page 325
... carbon steel in DSW saline waters are given in Table 8 . Corrosion rates of steel in waters from wells Tamar 3 and Tamar 10 were determined by weight - loss measurements in the lab . The values obtained are 0.25 to 0.33 mm / y ...
... carbon steel in DSW saline waters are given in Table 8 . Corrosion rates of steel in waters from wells Tamar 3 and Tamar 10 were determined by weight - loss measurements in the lab . The values obtained are 0.25 to 0.33 mm / y ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium