... waters including brackish water from a series of wells along the western escarpment fault of the Dead Sea rift valley . These wells are located in the Tamar , Admon , Amiaz , Zin and Yeelim fields . The waters are corrosive in nature ...
... waters including brackish water from a series of wells along the western escarpment fault of the Dead Sea rift valley . These wells are located in the Tamar , Admon , Amiaz , Zin and Yeelim fields . The waters are corrosive in nature ...
Page 328
... water ( Tamar 10 well ) . 1. Brackish water , pH 7.4 ; 2. Brackish water + 10 ppm H2S ( as Na2S ) , pH 5.0 ; 3. Brackish water + 10 ppm H2S ( as Na2S ) , pH 3.0 . 7. DISCUSSION 7.1 . Corrosion and Scaling Characteristics The corrosion ...
... water ( Tamar 10 well ) . 1. Brackish water , pH 7.4 ; 2. Brackish water + 10 ppm H2S ( as Na2S ) , pH 5.0 ; 3. Brackish water + 10 ppm H2S ( as Na2S ) , pH 3.0 . 7. DISCUSSION 7.1 . Corrosion and Scaling Characteristics The corrosion ...
Page 335
... brackish waters caused a drastic shift of the redox potential E ( ORP ) towards more electronegative cathodic values ... water has values in the range 0.10 to 0.60 volts . Natural formation of H2S in brines decreases the redox potential to ...
... brackish waters caused a drastic shift of the redox potential E ( ORP ) towards more electronegative cathodic values ... water has values in the range 0.10 to 0.60 volts . Natural formation of H2S in brines decreases the redox potential to ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum anaerobic Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing values vanadium