Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 27
Page 209
... boiler pipes , different corrosion conditions exist due to the following reasons : a . On the water side - Development of corrosion on the water side ( internal pipe wall ) can be due to incorrect water treatment with incomplete ...
... boiler pipes , different corrosion conditions exist due to the following reasons : a . On the water side - Development of corrosion on the water side ( internal pipe wall ) can be due to incorrect water treatment with incomplete ...
Page 228
... Boiler tubes A83 0.06 to 0.18 C 850 Boiler tubes for high pressure A192 0.06 to 0.18 C , 0.35 Si max 850 A210 0.27 C max 850 Table 6 ( cont . ) Common Name Boiler tubes Boiler tubes Boiler tubes for high 228 Vol . 9 , Nos . 3-4 , 1990 ...
... Boiler tubes A83 0.06 to 0.18 C 850 Boiler tubes for high pressure A192 0.06 to 0.18 C , 0.35 Si max 850 A210 0.27 C max 850 Table 6 ( cont . ) Common Name Boiler tubes Boiler tubes Boiler tubes for high 228 Vol . 9 , Nos . 3-4 , 1990 ...
Page 229
... Boiler tubes Boiler tubes Boiler tubes for high pressure Carbon - molybdenum boiler and ASTM Designation Pertinent Nominal Grade Composition , % Usual Maximum Service , Temp . F A178 C 0.35 C max 850 A226 850 A209 Tla 0.20 C , 0.50 Mo ...
... Boiler tubes Boiler tubes Boiler tubes for high pressure Carbon - molybdenum boiler and ASTM Designation Pertinent Nominal Grade Composition , % Usual Maximum Service , Temp . F A178 C 0.35 C max 850 A226 850 A209 Tla 0.20 C , 0.50 Mo ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium