Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 81
Page 18
... attack . An earlier review by Kulman 81 contends that coatings based on polyethylene or polyvinyl chloride are not readily susceptible to attack by soil microorganisms . A polyethylene layer wrapped loosely around cast - iron piping in ...
... attack . An earlier review by Kulman 81 contends that coatings based on polyethylene or polyvinyl chloride are not readily susceptible to attack by soil microorganisms . A polyethylene layer wrapped loosely around cast - iron piping in ...
Page 20
... attack . Epoxy coatings on steel tanks and bars were found to contain many species of fungi and bacteria , the most prolific microorganisms being aerobic , spore - forming , rod - shaped bacteria 99. Conversely , Pankhurst and co ...
... attack . Epoxy coatings on steel tanks and bars were found to contain many species of fungi and bacteria , the most prolific microorganisms being aerobic , spore - forming , rod - shaped bacteria 99. Conversely , Pankhurst and co ...
Page 270
... attack. EDXA of the corrosion products were compared with those reported for 90/10 dipper-nickel alloy. According to ... attack due to the combined effects of corrosion and erosion (impingement attack) produced as a consequence of the ...
... attack. EDXA of the corrosion products were compared with those reported for 90/10 dipper-nickel alloy. According to ... attack due to the combined effects of corrosion and erosion (impingement attack) produced as a consequence of the ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium