... anodic depolarization under aerobic conditions , hence promoting corrosion . Corrosion was also stimulated , to a smaller degree , by cathodic depolarization caused by metabolites formed by film - forming microorganisms . Anodic ...
... anodic depolarization under aerobic conditions , hence promoting corrosion . Corrosion was also stimulated , to a smaller degree , by cathodic depolarization caused by metabolites formed by film - forming microorganisms . Anodic ...
Page 109
... Anodic -04 -06 Cathodic -0.8 Anodic Cathodic 50 TOO O 50 100 Current density , μA cm2 • FIGURE 4 · Anodic and cathodic polarization curves for mild steel at 30 C ) , from Booth and Tiller , 1963 ) . Left : anodic compartment sterile ...
... Anodic -04 -06 Cathodic -0.8 Anodic Cathodic 50 TOO O 50 100 Current density , μA cm2 • FIGURE 4 · Anodic and cathodic polarization curves for mild steel at 30 C ) , from Booth and Tiller , 1963 ) . Left : anodic compartment sterile ...
Page 325
... anodic and cathodic polarization plots ( Tables 7 and 8 ) . Figure 12 shows typical anodic and cathodic polarization curves of carbon steel in saline water received from Admon 5. The influence of H2S addition on anodic and cathodic ...
... anodic and cathodic polarization plots ( Tables 7 and 8 ) . Figure 12 shows typical anodic and cathodic polarization curves of carbon steel in saline water received from Admon 5. The influence of H2S addition on anodic and cathodic ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum anaerobic Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing values vanadium