Page 57
... aluminum , titanium and copper - nickel , as well as stainless steel , was undertaken by Little 285,286 Seawater pumped through the exchangers caused a rapid development of biofouling and corrosion of copper - nickel and aluminum ...
... aluminum , titanium and copper - nickel , as well as stainless steel , was undertaken by Little 285,286 Seawater pumped through the exchangers caused a rapid development of biofouling and corrosion of copper - nickel and aluminum ...
Page 58
... aluminum salts , as well as magnesium , calcium and iron , over the aluminum tube interior surface . After two weeks , several types of bacteria including those of the filamentous type were observed in colonies on the tube surface , and ...
... aluminum salts , as well as magnesium , calcium and iron , over the aluminum tube interior surface . After two weeks , several types of bacteria including those of the filamentous type were observed in colonies on the tube surface , and ...
Page 59
... aluminum . Hagiwara 295 , 296 observed corrosion of various surface - treated aluminum alloys in seawater and discovered that barnacle attachment caused the formation of deep pits close to their shells and the dissolution of aluminum ...
... aluminum . Hagiwara 295 , 296 observed corrosion of various surface - treated aluminum alloys in seawater and discovered that barnacle attachment caused the formation of deep pits close to their shells and the dissolution of aluminum ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium