Page 135
Biological ' corrosion of LIST OF PUBLICATIONS and electrochemical aluminium " , R. C. factors involved in microbial Salvarezza and H.A. Videla , Anal . Asoc . Quim . Argentina , 66 , 317 ( 1978 ) . - · " Corrosion of aluminium and its ...
Biological ' corrosion of LIST OF PUBLICATIONS and electrochemical aluminium " , R. C. factors involved in microbial Salvarezza and H.A. Videla , Anal . Asoc . Quim . Argentina , 66 , 317 ( 1978 ) . - · " Corrosion of aluminium and its ...
Page 114
Aluminium Anodes Pure aluminium galvanic anodes are not employed in fresh wa- ter installations because of the possibility of passivity . In the USA , aluminium - tin - bismuth ( Al - Sn - Bi ) and aluminium - zinc - tin ( Al - Zn- Sn ) ...
Aluminium Anodes Pure aluminium galvanic anodes are not employed in fresh wa- ter installations because of the possibility of passivity . In the USA , aluminium - tin - bismuth ( Al - Sn - Bi ) and aluminium - zinc - tin ( Al - Zn- Sn ) ...
Page 116
In practice mainly aluminium has been used in the form of con- sumable anodes in cathodic protection of domestic water installa- tions . Other metals such as steel , zinc and copper deteriorate the water quality , e.g. , taste , colour ...
In practice mainly aluminium has been used in the form of con- sumable anodes in cathodic protection of domestic water installa- tions . Other metals such as steel , zinc and copper deteriorate the water quality , e.g. , taste , colour ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium