Page 192
Resistant Alloy ABSTRACT A new nickel based age - hardenable highly corrosion resistant alloy has been developed for sour gas service . INCONEL * alloy 725 ( UNS N07725 ) can be age - hardened to 0.2 % yield strengths of 120 ksi ( 827 ...
Resistant Alloy ABSTRACT A new nickel based age - hardenable highly corrosion resistant alloy has been developed for sour gas service . INCONEL * alloy 725 ( UNS N07725 ) can be age - hardened to 0.2 % yield strengths of 120 ksi ( 827 ...
Page 196
Resistant Alloy and hardnesses up to 41.5 HRc did not crack when coupled to carbon steel for 720 to 1000 hours . Alloy 625 PLUS and alloy 718 , yield strength 130 ksi ( 896 MPa ) and hardness HRc 34/35 , did not crack in 720 hours of ...
Resistant Alloy and hardnesses up to 41.5 HRc did not crack when coupled to carbon steel for 720 to 1000 hours . Alloy 625 PLUS and alloy 718 , yield strength 130 ksi ( 896 MPa ) and hardness HRc 34/35 , did not crack in 720 hours of ...
Page 270
Allay Behavior in Artificial Chloride Solutions ABSTRACT Relevant differences between the electrochemical responses of 70/30 copper-nickel alloy in natural seawater and artificial solutions were found by using different electrochemical ...
Allay Behavior in Artificial Chloride Solutions ABSTRACT Relevant differences between the electrochemical responses of 70/30 copper-nickel alloy in natural seawater and artificial solutions were found by using different electrochemical ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CORROSION REVIEWS | 3 |
BIOCORROSION IN WATER | 31 |
SulphateReducing Bacteria and Anaerobic Corrosion | 104 |
Copyright | |
53 other sections not shown
Other editions - View all
Common terms and phrases
acid activity addition alloy anaerobic anodic applied areas Association ASTM attack bacteria behaviour biological brackish carbon steel cathodic cause chemical chloride coating composition concentration containing copper corrosion products corrosion rate Dead Sea decrease deposits Desulfovibrio determined developed dissolved effect electrochemical Engineers environment et al field Figure flow formation formed fouling fuel hydrogen important increase indicate industrial inhibitor International iron laboratory layer levels lower Marine materials measurements mechanism metal metal surface methods microbial microorganisms mild steel natural observed obtained occurs organisms oxide oxygen pipelines pipes pitting plant polarization potential present problem properties protective reaction reduce resistance Saline Waters salts samples scaling seawater shown shows soil solution species stainless steel steel structures sulfate-reducing bacteria sulfide sulphide sulphur surface Table techniques temperature tests tubing values various Videla