Resistant Alloy ABSTRACT A new nickel based age - hardenable highly corrosion resistant alloy has been developed for sour gas service . INCONEL * alloy 725 ( UNS NO7725 ) can be age - hardened to 0.2 % yield strengths of 120 ksi ( 827 ...
Resistant Alloy ABSTRACT A new nickel based age - hardenable highly corrosion resistant alloy has been developed for sour gas service . INCONEL * alloy 725 ( UNS NO7725 ) can be age - hardened to 0.2 % yield strengths of 120 ksi ( 827 ...
Page 196
... Alloy 625 PLUS and alloy 718 , yield strength 130 ksi ( 896 MPa ) and hardness HRc 34/35 , did not crack in 720 hours of exposure . Stress corrosion cracking data for C - rings evaluated in a 25 % NaCl + 0.5 % acetic acid + 120 psig H2S ...
... Alloy 625 PLUS and alloy 718 , yield strength 130 ksi ( 896 MPa ) and hardness HRc 34/35 , did not crack in 720 hours of exposure . Stress corrosion cracking data for C - rings evaluated in a 25 % NaCl + 0.5 % acetic acid + 120 psig H2S ...
Page 270
... alloy. According to the present results, the protective characteristics of the complex layers that were formed on 70/30 copper-nickel alloy surface could be altered by the microbial adhesion on the metal surface. Biofilms affect copper ...
... alloy. According to the present results, the protective characteristics of the complex layers that were formed on 70/30 copper-nickel alloy surface could be altered by the microbial adhesion on the metal surface. Biofilms affect copper ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium