Page 366
Table 4 shows the values of the inhibitor effectiveness , P % , for the three systems at concentrations of 1.5 g / kg , 2.0 g / kg and 3.0 g / kg ... Tables 5 , 6 and 7 give the same indications with reference to the product Rodine 213.
Table 4 shows the values of the inhibitor effectiveness , P % , for the three systems at concentrations of 1.5 g / kg , 2.0 g / kg and 3.0 g / kg ... Tables 5 , 6 and 7 give the same indications with reference to the product Rodine 213.
Page 14
Results from tests conducted at the National Fertilizer Devel- opment Center ( NFDC ) - Tennessee Valley Authority / 8 / are shown in Table 8. Type 316L stainless steel and 20 - type stainless steel ( Fe - 21Cr - 25Ni - 5Mo - 0.5Cu ) ...
Results from tests conducted at the National Fertilizer Devel- opment Center ( NFDC ) - Tennessee Valley Authority / 8 / are shown in Table 8. Type 316L stainless steel and 20 - type stainless steel ( Fe - 21Cr - 25Ni - 5Mo - 0.5Cu ) ...
Page 269
20 : Porosity measurements on matte unpassivated tinplate , a comparison of the corrosion potential and conductance results / 145 / . polarisation with those from the cathodic corrosion current method and the anodic method ( Table V ) .
20 : Porosity measurements on matte unpassivated tinplate , a comparison of the corrosion potential and conductance results / 145 / . polarisation with those from the cathodic corrosion current method and the anodic method ( Table V ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium