Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 11
Page 248
... after 5 , 7 and 10 years of exposition in the urban ambient . The previously found differences in morphology Table 2 ( cont . ) Dry , High Solar 248 Vol 9 , Nos . 3-4 , 1990 Electrochemical Response of Weathering RESULTS.
... after 5 , 7 and 10 years of exposition in the urban ambient . The previously found differences in morphology Table 2 ( cont . ) Dry , High Solar 248 Vol 9 , Nos . 3-4 , 1990 Electrochemical Response of Weathering RESULTS.
Page 254
... solar radiation ; B. Subtropical ; C. Urban ; D. Marine . Weathering steels , at t = 0 , -550 mV ( SCE ) ; --- non - alloyed steels , at t = 0 , -390 mV ( SCE ) 200 100 0 - 100 -200 -300 - 400 - 254 Vol . 9 , Nos . 3-4 , 1990 ...
... solar radiation ; B. Subtropical ; C. Urban ; D. Marine . Weathering steels , at t = 0 , -550 mV ( SCE ) ; --- non - alloyed steels , at t = 0 , -390 mV ( SCE ) 200 100 0 - 100 -200 -300 - 400 - 254 Vol . 9 , Nos . 3-4 , 1990 ...
Page 256
TABLE 3 Test Sites Rural Dry - High Solar Radiation Rural Subtropical Urban Marine Esce ( V ) 12 8 4 0 -.4 -8. REGRESSION VALUES FOR CONSTANTS k AND a IN THE EQUATION W = k.t " ( SKYWARD FACE ONLY ) and Plain C Steels in Different ...
TABLE 3 Test Sites Rural Dry - High Solar Radiation Rural Subtropical Urban Marine Esce ( V ) 12 8 4 0 -.4 -8. REGRESSION VALUES FOR CONSTANTS k AND a IN THE EQUATION W = k.t " ( SKYWARD FACE ONLY ) and Plain C Steels in Different ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium