Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 9
Page 201
... Dual Age TABLE 6 None None 106.0 158.4 39.3 54.9 " 1. " 1400 ° F / 6h / AC + 34.5 119.0 172.2 32.5 Well Age 1375 ° F Dual Age 40.0 128.6 184.6 27.5 1850 ° F 1400 ° F Dual Age 39.0 133.0 186.0 25.5 1850 ° F 1400 ° F Dual Age + 41.5 130.8 ...
... Dual Age TABLE 6 None None 106.0 158.4 39.3 54.9 " 1. " 1400 ° F / 6h / AC + 34.5 119.0 172.2 32.5 Well Age 1375 ° F Dual Age 40.0 128.6 184.6 27.5 1850 ° F 1400 ° F Dual Age 39.0 133.0 186.0 25.5 1850 ° F 1400 ° F Dual Age + 41.5 130.8 ...
Page 203
... Dual Age 38.0 129.0 185.0 31.5 53.5 77.0 1350 ° F Dual Age 40.0 136.4 184.4 28.0 49.0 " 1375 ° F Dual Age 37.0 132.4 186.9 27.0 44.0 1850 ° F 1375 ° F Dual Age * 36.5 139.7 187.4 26.0 41.5 " 1 1400 ° F Dual Age 37.5 139.0 186.5 27.0 38.0 " ...
... Dual Age 38.0 129.0 185.0 31.5 53.5 77.0 1350 ° F Dual Age 40.0 136.4 184.4 28.0 49.0 " 1375 ° F Dual Age 37.0 132.4 186.9 27.0 44.0 1850 ° F 1375 ° F Dual Age * 36.5 139.7 187.4 26.0 41.5 " 1 1400 ° F Dual Age 37.5 139.0 186.5 27.0 38.0 " ...
Page 204
... Dual Age 38.1 142.9 196.8 28.6 48.8 " 1375 ° F Dual Age 38.5 146.4 196.1 28.0 41.4 56.0 " 1400 ° F Dual Age 38.9 148.8 199.1 25.7 39.6 35.0 HEAT TREATMENT : TABLE 8 Hardness ( RC ) " 1400 ° F. Resistant Alloy ROOM TEMPERATURE TENSILE AND ...
... Dual Age 38.1 142.9 196.8 28.6 48.8 " 1375 ° F Dual Age 38.5 146.4 196.1 28.0 41.4 56.0 " 1400 ° F Dual Age 38.9 148.8 199.1 25.7 39.6 35.0 HEAT TREATMENT : TABLE 8 Hardness ( RC ) " 1400 ° F. Resistant Alloy ROOM TEMPERATURE TENSILE AND ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium