... Desulfovibrio are variously found in Artic , temperate and tropical environments , in both fresh and salt water , hot springs , oil wells as well as in the soil and sea and river - bottom mud and occur either singly or 19 , 20 in chains ...
... Desulfovibrio are variously found in Artic , temperate and tropical environments , in both fresh and salt water , hot springs , oil wells as well as in the soil and sea and river - bottom mud and occur either singly or 19 , 20 in chains ...
Page 23
... Desulfovibrio desulfuricans and Desulfotomaculum , anaerobic , sulfate - reducing bacteria , cause corrosion of ferrous metals . Postgate and others describe the metabolism of sulfate by Desulfovibrio and Desulfotomaculum at length . In ...
... Desulfovibrio desulfuricans and Desulfotomaculum , anaerobic , sulfate - reducing bacteria , cause corrosion of ferrous metals . Postgate and others describe the metabolism of sulfate by Desulfovibrio and Desulfotomaculum at length . In ...
Page 64
... Desulfovibrio , Desulfovibrio in pipe deposits and sludge , a sterile cotton - tipped swab is used to remove some of the material , which is then dropped into a bottle of this medium . Another technique involves insertion of an agar ...
... Desulfovibrio , Desulfovibrio in pipe deposits and sludge , a sterile cotton - tipped swab is used to remove some of the material , which is then dropped into a bottle of this medium . Another technique involves insertion of an agar ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium