Page 270
Alloy Behavior in Artificial Chloride Solutions ABSTRACT Relevant differences between the electrochemical responses of 70/30 copper - nickel alloy in natural seawater and artificial solutions were found by using different ...
Alloy Behavior in Artificial Chloride Solutions ABSTRACT Relevant differences between the electrochemical responses of 70/30 copper - nickel alloy in natural seawater and artificial solutions were found by using different ...
Page 288
Alloy Behavior in Artificial Chloride Solutions predominated along the year ... 70/30 copper- nickel alloy is reduced with respect to stainless steel due to the toxic characteristics of the substrata . The corrosion ... 70/30 Copper - Nickel.
Alloy Behavior in Artificial Chloride Solutions predominated along the year ... 70/30 copper- nickel alloy is reduced with respect to stainless steel due to the toxic characteristics of the substrata . The corrosion ... 70/30 Copper - Nickel.
Page 289
... nickel and iron and accompanied by some components of the polluted seawater like sulphur , silicon , magnesium , calcium , and chlorides / 4,24 / . Data corresponding to 70/30 copper - nickel alloy are in good agreement with these ...
... nickel and iron and accompanied by some components of the polluted seawater like sulphur , silicon , magnesium , calcium , and chlorides / 4,24 / . Data corresponding to 70/30 copper - nickel alloy are in good agreement with these ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium