Corrosion Reviews, Volumes 9-10Scientific Publications Division, Freund Publishing House, 1990 |
From inside the book
Results 1-3 of 23
Page 270
... 70/30 copper-nickel alloy in natural seawater and artificial solutions were found by using different electrochemical techniques. SEM observations were used to assess microfouling settlement and the metal attack. EDXA of the corrosion ...
... 70/30 copper-nickel alloy in natural seawater and artificial solutions were found by using different electrochemical techniques. SEM observations were used to assess microfouling settlement and the metal attack. EDXA of the corrosion ...
Page 270
... alloy in natural seawater and artificial solutions were found by using different electrochemical techniques . SEM observations were used to assess microfouling settlement and the metal attack . EDXA of the corrosion ... 70/30 Copper - Nickel.
... alloy in natural seawater and artificial solutions were found by using different electrochemical techniques . SEM observations were used to assess microfouling settlement and the metal attack . EDXA of the corrosion ... 70/30 Copper - Nickel.
Page 289
marked differences in copper , iron , nickel , and sulphur content from one to another region / 14 / . EDXA , ESCA and Auger surface analyses of 90/10 copper - nickel alloy showed that the outer porous layer is mainly Cu2 ( OH ) 3Cl ...
marked differences in copper , iron , nickel , and sulphur content from one to another region / 14 / . EDXA , ESCA and Auger surface analyses of 90/10 copper - nickel alloy showed that the outer porous layer is mainly Cu2 ( OH ) 3Cl ...
Other editions - View all
Common terms and phrases
70/30 copper-nickel alloy acid aerobic algae alloy aluminum Anaerobic Corrosion anodic aqueous Association of Corrosion ASTM attack Basin Saline Waters behaviour biocorrosion Biodeterioration biofilm Biofouling Biologically Induced Corrosion boiler brackish water carbon steel cathodic chemical chloride coating components concentration containing copper Corrosion Engineers corrosion potential corrosion process corrosion products corrosion rate crevice corrosion Dead Sea Dead Sea Basin depolarization deposits Desulfovibrio dissolved oxygen Dual Age effect electrochemical environment film fouling fuel H. A. Videla hydrogen sulfide immersed inhibitor ions iron sulphide laboratory layer Marine materials measurements mechanism metal surface Microbial Corrosion microfouling microorganisms mild steel molten salts NACE organisms oxide pipelines pipes piping materials pitting pitting corrosion polarization resistance present protective reaction S.C. Dexter Saline Waters Salvarezza samples Sdom Sea Basin Saline seawater soil solution stainless steel sulfate-reducing bacteria sulfur sulphate sulphide sulphur Table Tamar techniques temperature Thiobacillus tubing vanadium