Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 19
Page 210
... stainless steels became anodic during the first three days . After one months , it can be observed ( Fig . 1 ) that the potentials of 316L and 316L + Sn remained anodic whereas those of 316L + Cu and 316L + As returned to the cathodic ...
... stainless steels became anodic during the first three days . After one months , it can be observed ( Fig . 1 ) that the potentials of 316L and 316L + Sn remained anodic whereas those of 316L + Cu and 316L + As returned to the cathodic ...
Page 220
on Stainless Alloys in Seawater ABSTRACT A range of stainless steels and nickel base alloys has been tested for crevice corrosion in strongly oxidising or reducing seawater environments : ( i ) natural seawater with high chlorine ...
on Stainless Alloys in Seawater ABSTRACT A range of stainless steels and nickel base alloys has been tested for crevice corrosion in strongly oxidising or reducing seawater environments : ( i ) natural seawater with high chlorine ...
Page 222
on Stainless Alloys in Seawater solution into a 5 m3 tank . The residual ... steels and two nickel base alloys , the chemical compositions of which are ... stainless steels and nickel base alloys were tested : the stainless steels ...
on Stainless Alloys in Seawater solution into a 5 m3 tank . The residual ... steels and two nickel base alloys , the chemical compositions of which are ... stainless steels and nickel base alloys were tested : the stainless steels ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich