Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 22
Page 11
... specimens . Each digitized ultrasonic signal was averaged over 64 readings to improve the signal - to - noise ratio . One specimen was then destructively tested while the rest of the specimens were put back into the water until the next ...
... specimens . Each digitized ultrasonic signal was averaged over 64 readings to improve the signal - to - noise ratio . One specimen was then destructively tested while the rest of the specimens were put back into the water until the next ...
Page 224
... specimens were used : coupons and electrodes . The coupons were rectangular specimens ( 200x70 mm ) as shown in Figure 1 . When fabricating the coupons , two plates were butt welded ( GTAW ) to form the specimen . The welding was done ...
... specimens were used : coupons and electrodes . The coupons were rectangular specimens ( 200x70 mm ) as shown in Figure 1 . When fabricating the coupons , two plates were butt welded ( GTAW ) to form the specimen . The welding was done ...
Page 232
... specimens in places where rust spots could be seen after the exposure . A section of such a pit is shown in Figure 14 . 3.3.2 . Sulphide Polluted Seawater . At the end of the test , there were white but not adherent deposits on specimens ...
... specimens in places where rust spots could be seen after the exposure . A section of such a pit is shown in Figure 14 . 3.3.2 . Sulphide Polluted Seawater . At the end of the test , there were white but not adherent deposits on specimens ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich