Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 69
Page 209
... solution containing phosphates in order to open the spores and to reactivate the bacteria . After that , bacteria were cultivated in phosphate media and inoculated in the solution . Culture media was also added to the solution on a ...
... solution containing phosphates in order to open the spores and to reactivate the bacteria . After that , bacteria were cultivated in phosphate media and inoculated in the solution . Culture media was also added to the solution on a ...
Page 251
Results of gravimetric tests in three different solutions are shown in Table 1. A visual examination of metallic plates after 14 days of immersion in solution B showed a slightly dark film covering copper and brass surfaces , while tin ...
Results of gravimetric tests in three different solutions are shown in Table 1. A visual examination of metallic plates after 14 days of immersion in solution B showed a slightly dark film covering copper and brass surfaces , while tin ...
Page 257
... solution B showed better performance than solution A under standard specifications . No signs of pitting corrosion or cavitation were detected . Weight loss values for aluminium and ferrous alloy decreased . This result qualified the ...
... solution B showed better performance than solution A under standard specifications . No signs of pitting corrosion or cavitation were detected . Weight loss values for aluminium and ferrous alloy decreased . This result qualified the ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich