Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 25
Page 128
... selected ( Table 13 ) were red iron oxide , aluminium powder and zinc phosphate . Two series of anticorrosive coatings were prepared , pigmented with zinc tetroxychromate ( Table 14 ) and zinc phosphate ( Table 15 ) . The binder was ...
... selected ( Table 13 ) were red iron oxide , aluminium powder and zinc phosphate . Two series of anticorrosive coatings were prepared , pigmented with zinc tetroxychromate ( Table 14 ) and zinc phosphate ( Table 15 ) . The binder was ...
Page 138
... selected as the film forming material , and micaceous iron oxide as the basic pigment , so as to give an intermediate coating ( sealer ) suitable for applying over an anticorrosive coating in a system designed to protect a metallic ...
... selected as the film forming material , and micaceous iron oxide as the basic pigment , so as to give an intermediate coating ( sealer ) suitable for applying over an anticorrosive coating in a system designed to protect a metallic ...
Page 183
... selected and applied on shore to new constructions ; in addition , the original coating system should provide for easy maintenance under all conditions , including adverse ones . In general , corrosion prevention in underwater areas can ...
... selected and applied on shore to new constructions ; in addition , the original coating system should provide for easy maintenance under all conditions , including adverse ones . In general , corrosion prevention in underwater areas can ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich