Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 63
Page 38
... resistance of the film ( R ) increased . At 75 mVs1 the maximum resistance ( R ) was observed with 0.2M Na2 CO3 . The subsequent decrease in resistance with carbonate suggested that desorption was predominant with increasing carbonate ...
... resistance of the film ( R ) increased . At 75 mVs1 the maximum resistance ( R ) was observed with 0.2M Na2 CO3 . The subsequent decrease in resistance with carbonate suggested that desorption was predominant with increasing carbonate ...
Page 89
... resistance , resistance to the passage of ions , resistance to osmotic phenomena , resistance to weather , behaviour against chemicals , good adhesion , etc. 4.4 . Economic and technical aspects In recent years ships and offshore the ...
... resistance , resistance to the passage of ions , resistance to osmotic phenomena , resistance to weather , behaviour against chemicals , good adhesion , etc. 4.4 . Economic and technical aspects In recent years ships and offshore the ...
Page 175
... resistance ) since for PVC equal to or higher than 40 % ( these samples included a higher content of inhibitive pigment ) , the efficiency of protection decreased ( greater degree of rusting and lower ohmic resistance ) . Coating ...
... resistance ) since for PVC equal to or higher than 40 % ( these samples included a higher content of inhibitive pigment ) , the efficiency of protection decreased ( greater degree of rusting and lower ohmic resistance ) . Coating ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich