... potential from the open circuit potential to -1000 mV / SCE , then returning towards the noble potential until either the current reached .001 amp / cm2 or until the pitting potential was reached . Electrochemical impedance spectroscopy ...
... potential from the open circuit potential to -1000 mV / SCE , then returning towards the noble potential until either the current reached .001 amp / cm2 or until the pitting potential was reached . Electrochemical impedance spectroscopy ...
Page 211
... potential of 316L became more noble in the solution without bacteria while , in the solution containing bacteria , its open circuit potential went to the cathodic potentials . The 316L + As stainless steel showed contrasting behavior ...
... potential of 316L became more noble in the solution without bacteria while , in the solution containing bacteria , its open circuit potential went to the cathodic potentials . The 316L + As stainless steel showed contrasting behavior ...
Page 214
... potentials had a constant behavior . The potentials remained between -180 mV / SCE and -350 mV / SCE ( Fig . 6 ) . The open circuit potential of 316L went to the anodic potentials during the first week , after which the potential joined ...
... potentials had a constant behavior . The potentials remained between -180 mV / SCE and -350 mV / SCE ( Fig . 6 ) . The open circuit potential of 316L went to the anodic potentials during the first week , after which the potential joined ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich