Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 41
Page 49
... particle size distribution / 14 / . Micronized ZP has acquired ever increasing significance since it disperses better , sediments less and its content in the paint formulation may be reduced . This is probably due to the smaller particle ...
... particle size distribution / 14 / . Micronized ZP has acquired ever increasing significance since it disperses better , sediments less and its content in the paint formulation may be reduced . This is probably due to the smaller particle ...
Page 140
... particle diameter . In general a low average diameter was associated with a broad size distribution , which favoured a high packing density of pigment particle in the coating film . The average particle size values for the micaceous ...
... particle diameter . In general a low average diameter was associated with a broad size distribution , which favoured a high packing density of pigment particle in the coating film . The average particle size values for the micaceous ...
Page 147
... particle size ( 49.3 % CPVC approximately ) are more appropriate . It is important to realize that , for the two film thicknesses studied , the lower permeability per unit film thickness is observed for the 100-110 μm thickness . The ...
... particle size ( 49.3 % CPVC approximately ) are more appropriate . It is important to realize that , for the two film thicknesses studied , the lower permeability per unit film thickness is observed for the 100-110 μm thickness . The ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich