... paint , g : Red iron oxide . 5.6 Paint Co 0.0 .... Barytes 10.9 Paint C. 0.4 ... Grade 10 chlorinated rubber . 15.2 Paint C2 . 0.8 42 % chlorinated paraffin ............... .. 5.2 Paint C3 .. 1.2 70 % chlorinated paraffin 10.0 Paint C4 ...
... paint , g : Red iron oxide . 5.6 Paint Co 0.0 .... Barytes 10.9 Paint C. 0.4 ... Grade 10 chlorinated rubber . 15.2 Paint C2 . 0.8 42 % chlorinated paraffin ............... .. 5.2 Paint C3 .. 1.2 70 % chlorinated paraffin 10.0 Paint C4 ...
Page 179
... paint , 120 μm d.f.t. ( one coat ) High - build vinyl paint , 100 μm d.f.t. ( one coat ) Vinyl acrylic paint , 50 μm d.f.t. ( one coat ) 2. Main exterior decks , helideck Primer : Build coat : Finish : 3. Submerged part Zinc silicate ...
... paint , 120 μm d.f.t. ( one coat ) High - build vinyl paint , 100 μm d.f.t. ( one coat ) Vinyl acrylic paint , 50 μm d.f.t. ( one coat ) 2. Main exterior decks , helideck Primer : Build coat : Finish : 3. Submerged part Zinc silicate ...
Page 180
... paint , 300 m d.f.t. ( two coats ) Usually no coating is necessary 6. Machinery area ( machinery , decks , sides and overheads ) Primer : Build coat : Zinc phosphate pigmented urethane - modified alkyd primer , 60 μm d.f.t. ( one coat ) ...
... paint , 300 m d.f.t. ( two coats ) Usually no coating is necessary 6. Machinery area ( machinery , decks , sides and overheads ) Primer : Build coat : Zinc phosphate pigmented urethane - modified alkyd primer , 60 μm d.f.t. ( one coat ) ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich