Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 60
Page 140
... formulated with PVC 55 % , which requires a shorter time than that formulated with PVC 50 % . This could be attributed to the lower apparent viscosity shown by a coating formulated with PVC higher than the critical pigment volume ...
... formulated with PVC 55 % , which requires a shorter time than that formulated with PVC 50 % . This could be attributed to the lower apparent viscosity shown by a coating formulated with PVC higher than the critical pigment volume ...
Page 148
... formulated as barriers , in order to isolate the metallic substrate from the environment . However , all organic coatings are more or less permeable to moisture and pollutants , and are therefore not perfect barriers . Many coating ...
... formulated as barriers , in order to isolate the metallic substrate from the environment . However , all organic coatings are more or less permeable to moisture and pollutants , and are therefore not perfect barriers . Many coating ...
Page 175
... formulated with PVC 30 % ( inhibitive pigment 6 % ) showed the best efficiency of this series . • Corrosion inhibitor / inert pigment ratio 30/70 . The CPVC value increased compared to samples formulated with 20/80 ratio ; the results ...
... formulated with PVC 30 % ( inhibitive pigment 6 % ) showed the best efficiency of this series . • Corrosion inhibitor / inert pigment ratio 30/70 . The CPVC value increased compared to samples formulated with 20/80 ratio ; the results ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich