Page 140
... film thickness , respectively ) . It can also be observed in these figures that coating formulated with PVC 55 % requires a shorter dispersion time than that with PVC 50 % to reach a similar average particle size , although it shows a ...
... film thickness , respectively ) . It can also be observed in these figures that coating formulated with PVC 55 % requires a shorter dispersion time than that with PVC 50 % to reach a similar average particle size , although it shows a ...
Page 147
... film thickness is observed for the 100-110 μm thickness . The influence of film thickness on critical pigment volume concentration is attributed to the restrictive effect of the free coating surface on the pigment's ability to achieve a ...
... film thickness is observed for the 100-110 μm thickness . The influence of film thickness on critical pigment volume concentration is attributed to the restrictive effect of the free coating surface on the pigment's ability to achieve a ...
Page 170
... film's porosity ( lower cathodic protective activity ) . On the other hand , a polar epoxy binder wets zinc ... thickness , due to the fact that zinc - rich coatings are porous when applied , the protection is only galvanic during their early ...
... film's porosity ( lower cathodic protective activity ) . On the other hand , a polar epoxy binder wets zinc ... thickness , due to the fact that zinc - rich coatings are porous when applied , the protection is only galvanic during their early ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich