Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 29
Page 92
... efficiency of the protective system and decrease costs . Also , a conventional system will give good performance when coatings are applied on surfaces with improved preparation . 5. PRIMERS AND ANTICORROSIVE COATINGS 5.1 . Shop primers ...
... efficiency of the protective system and decrease costs . Also , a conventional system will give good performance when coatings are applied on surfaces with improved preparation . 5. PRIMERS AND ANTICORROSIVE COATINGS 5.1 . Shop primers ...
Page 175
... efficiency of this series . • Corrosion inhibitor / inert pigment ratio 30/70 . The CPVC value increased compared to samples formulated with 20/80 ratio ; the results ranged from 34 to 36 % . The coatings in this series exhibited a ...
... efficiency of this series . • Corrosion inhibitor / inert pigment ratio 30/70 . The CPVC value increased compared to samples formulated with 20/80 ratio ; the results ranged from 34 to 36 % . The coatings in this series exhibited a ...
Page 176
... efficiency to be obtained ; however , above a given ratio dependent on PVC , the efficiency was practically unchanged ( similar degree of rusting ) . The coating with the highest efficiency ( degree of rusting 9 ) were formulated with ...
... efficiency to be obtained ; however , above a given ratio dependent on PVC , the efficiency was practically unchanged ( similar degree of rusting ) . The coating with the highest efficiency ( degree of rusting 9 ) were formulated with ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich