Page 220
... crevice corrosion after 95 days of exposure . In chlorinated water , only the S32654 steel ( 654 SMOTм ( 1 ) ) was unaffected by crevice corrosion . The other materials ( S31254 , S32750 , N06625 and N10276 ) were attacked by crevice ...
... crevice corrosion after 95 days of exposure . In chlorinated water , only the S32654 steel ( 654 SMOTм ( 1 ) ) was unaffected by crevice corrosion . The other materials ( S31254 , S32750 , N06625 and N10276 ) were attacked by crevice ...
Page 232
... crevice corrosion under the gaskets , all alloys except S32654 were attacked by other types of corrosion . In the gas phase above the water level , all alloys except S32654 and N10276 were slightly etched at the mounting holes of the ...
... crevice corrosion under the gaskets , all alloys except S32654 were attacked by other types of corrosion . In the gas phase above the water level , all alloys except S32654 and N10276 were slightly etched at the mounting holes of the ...
Page 240
... crevice corrosion is to be expected on S32750 and $ 31254 if the temperature or the chlorine concentration exceeds certain limits : thus , at 45 ° C , 2 mg.1-1 chlorine will cause crevice corrosion on both these alloys / 1,2 / . As ...
... crevice corrosion is to be expected on S32750 and $ 31254 if the temperature or the chlorine concentration exceeds certain limits : thus , at 45 ° C , 2 mg.1-1 chlorine will cause crevice corrosion on both these alloys / 1,2 / . As ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich