Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 38
Page 52
... binder . If the binder fails , the influence of the inhibitive pigment can be observed . For instance , there were not important differences among the anticorrosive pigments when epoxy and polyurethane were employed as binders . With ...
... binder . If the binder fails , the influence of the inhibitive pigment can be observed . For instance , there were not important differences among the anticorrosive pigments when epoxy and polyurethane were employed as binders . With ...
Page 116
... binder is present to fill the voids between pigment particles . When this value is greater than CPVC , the binder is not enough to fill all the voids ; on the other hand , a PVC value less than CPVC means an excess of binder . Taking ...
... binder is present to fill the voids between pigment particles . When this value is greater than CPVC , the binder is not enough to fill all the voids ; on the other hand , a PVC value less than CPVC means an excess of binder . Taking ...
Page 168
... binder Epoxy Film thickness 45-50 um 75-80 um Particle diameter 4 um 8 um 4 um 8 um Dispersion time 30 s . 180 s . 30s . 180 s . 30 s . 180 s . 30 s . 180 s . Zinc content 70 % 75 % 80 % 85 % 90 % 02677 03 02 13789 01357 92456 03567 01 ...
... binder Epoxy Film thickness 45-50 um 75-80 um Particle diameter 4 um 8 um 4 um 8 um Dispersion time 30 s . 180 s . 30s . 180 s . 30 s . 180 s . 30 s . 180 s . Zinc content 70 % 75 % 80 % 85 % 90 % 02677 03 02 13789 01357 92456 03567 01 ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich