... anodic peaks and two cathodic peaks are observed ; these features have been discussed elsewhere / 6,7 / . The voltammetric characteristics are unaffected by the presence of carbonates except that the third cathodic peak appeared as a ...
... anodic peaks and two cathodic peaks are observed ; these features have been discussed elsewhere / 6,7 / . The voltammetric characteristics are unaffected by the presence of carbonates except that the third cathodic peak appeared as a ...
Page 35
concentration from 0.1 M to 0.2 M , the cyclic voltammogram exhibited an additional anodic peak at 0.485 V ( II ) , at 50 mVs1 , which disappeared at higher v . With an increase in concentration above 0.3 M Na2CO3 , the second anodic ...
concentration from 0.1 M to 0.2 M , the cyclic voltammogram exhibited an additional anodic peak at 0.485 V ( II ) , at 50 mVs1 , which disappeared at higher v . With an increase in concentration above 0.3 M Na2CO3 , the second anodic ...
Page 36
additional anodic peak appeared at -1100 mV . This peak potential varied with log ( sweep rate ) with a slope of 70 mV decade and with log ( carbonate ions ) , with slope of 30 mV decade - 1 . These suggested the incorporation of ...
additional anodic peak appeared at -1100 mV . This peak potential varied with log ( sweep rate ) with a slope of 70 mV decade and with log ( carbonate ions ) , with slope of 30 mV decade - 1 . These suggested the incorporation of ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich