Corrosion Reviews, Volume 13Scientific Publications Division, Freund Publishing House, 1995 |
From inside the book
Results 1-3 of 88
Page 128
... ( Table 14 ) and zinc phosphate ( Table 15 ) . The binder was based on a vinyl resin ( copolymer of vinyl chloride - vinyl acetate modified with polyvinyl alcohol ) . Tricresyl phosphate and diisodecyl phthalate were used as plasticisers ...
... ( Table 14 ) and zinc phosphate ( Table 15 ) . The binder was based on a vinyl resin ( copolymer of vinyl chloride - vinyl acetate modified with polyvinyl alcohol ) . Tricresyl phosphate and diisodecyl phthalate were used as plasticisers ...
Page 151
... Table 23. Micaceous iron oxide coatings with low pigmentation levels displayed a reduced film permeability . For pigment volume concentrations higher than the critical value ( Table 24 ) film permeability increased significantly as the ...
... Table 23. Micaceous iron oxide coatings with low pigmentation levels displayed a reduced film permeability . For pigment volume concentrations higher than the critical value ( Table 24 ) film permeability increased significantly as the ...
Page 163
... Table 32 . Type of binder . Two binders were used in the formulations / 110-113 / - epoxy and ethyl silicate ( Table 33 ) . Dispersion time . Zinc dust was incorporated in the binders , employing a high - speed disperser ( Table 34 ) ...
... Table 32 . Type of binder . Two binders were used in the formulations / 110-113 / - epoxy and ethyl silicate ( Table 33 ) . Dispersion time . Zinc dust was incorporated in the binders , employing a high - speed disperser ( Table 34 ) ...
Contents
ABSTRACT | 17 |
Engineering Applications | 65 |
ΙΑ paper presented at the Meeting of the Israeli Forum on Corrosion Tel Aviv | 79 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion anodic anticorrosive coatings applied Assoc ASTM average particle bacteria binder biofilm biofouling carbonate cathodic cathodic protection Chem chemical chlorinated rubber chromate coating film coating system composition corrosion control corrosion products corrosion rate coupons CPVC CPVC values crevice corrosion critical pigment volume d.f.t. one coat decrease degree of rusting diameter diisodecyl phthalate dispersing agent dry film thickness electrochemical electrode engineering environment epoxy ethyl silicate evaluate exposure Film permeability formulated Gulf of Mexico immersion increase infrastructure inhibitive pigment inhibitor ions lamellar micaceous iron marine corrosion materials metal surface micaceous iron oxide Microbial Corrosion mV/SCE obtained offshore open circuit potential paint pigment volume concentration plasticiser polarization primer protection redox Review rheological samples seawater shear rate shear stress showed sodium sodium chloride solution solvent specimens stainless steels structures studied substrate Table Technol temperature thixotropic tricresyl phosphate vinyl resin xylene zinc phosphate zinc-rich