... specimens shall be conditioned and tested in accordance with procedure A of ASTM D 618-61 , Stand- ard Methods of Conditioning Plastics and Electrical Insulating Materials for Testing.2 See footnote 1 , page 2 . 4.3 . Dimensions and ...
... specimens shall be conditioned and tested in accordance with procedure A of ASTM D 618-61 , Stand- ard Methods of Conditioning Plastics and Electrical Insulating Materials for Testing.2 See footnote 1 , page 2 . 4.3 . Dimensions and ...
Page 5
... specimens and on five transverse specimens using a testing speed of 2 inches per minute . The test results for the ... Specimen shape shall be in the form of a dumbbell as shown in figure 1. Transverse specimens , 1/4 inch long , shall ...
... specimens and on five transverse specimens using a testing speed of 2 inches per minute . The test results for the ... Specimen shape shall be in the form of a dumbbell as shown in figure 1. Transverse specimens , 1/4 inch long , shall ...
Page 6
... specimen for tubing of 0.200 inch to 0.090 inch inclusive . 4.6.4 . Tubing having an inside diameter less than 0.090 inch- Specimens shall be tested as filaments . Nonslip type loop knots shall be made in each end of the specimen so ...
... specimen for tubing of 0.200 inch to 0.090 inch inclusive . 4.6.4 . Tubing having an inside diameter less than 0.090 inch- Specimens shall be tested as filaments . Nonslip type loop knots shall be made in each end of the specimen so ...
Page 7
... specimen on a perforated tray , in an unrestrained position , in an oven for 3 hours at 2605 ° C ( 500 ± 9 ° F ) . Remove the tray and allow the specimen to cool to 23 ± 1 ° C ( 73.4 ± 1.8 ° F ) . Slip the specimen onto the mandrel and ...
... specimen on a perforated tray , in an unrestrained position , in an oven for 3 hours at 2605 ° C ( 500 ± 9 ° F ) . Remove the tray and allow the specimen to cool to 23 ± 1 ° C ( 73.4 ± 1.8 ° F ) . Slip the specimen onto the mandrel and ...
Common terms and phrases
acceptance ACCEPTORS accordance with ASTM American applicable Association ASTM D basis Bureau of Standards Calif Center Chemical Chicago Class committee Company complete compliance conditioned conforming consists Corporation Department of Commerce determined determined in accordance Development distributors divisions document electrical Engineering Standards Services established Fluorocarbon Government Grade Inch Inch Inch inclusive indicated individually industry inside diameter Institute intended interested less listed longitudinal mandrel Mass Materials maximum measurement Melting methods of test MICHIGAN Minimum proof pressure minus National Bureau Office of Engineering Ohio percent Philadelphia physical Pittsburgh plastic tubing points Polytetrafluoroethylene PTFE Procedures Processing Prod Programs promotes proposed provides PTFE tubing published purchaser Reference Representing requirements Research Road Rubber specified in table Stand statement strength and elongation technical Technology temperature tensile strength tested in accordance Type UNITED users Voluntary Product Standard wall thicknesses Washington weight
Bibliographic information
| Title | NBS Voluntary Product Standard |
| Author | United States. National Bureau of Standards |
| Contributor | United States. Dept. of Commerce |
| Publisher | U.S. Department of Commerce, National Bureau of Standards, 1972 |
| Original from | the University of Michigan |
| Digitized | 18 Apr 2006 |
| Export Citation | BiBTeX EndNote RefMan |