The objective of a Voluntary Prod . uct Standard is to establish requirements which are in accordance with the ... Purchasers may order products that comply with Voluntary Product Standards and determine for themselves that their ...
The objective of a Voluntary Prod . uct Standard is to establish requirements which are in accordance with the ... Purchasers may order products that comply with Voluntary Product Standards and determine for themselves that their ...
Page 2
Dimensions and tolerances — The dimensions and tolerances of the tubing shall be as specified in table 1 or 2 when the tubing is measured in accordance with 4.3 . wire gage 19 1 Later issues of the ASTM publications referenced in this ...
Dimensions and tolerances — The dimensions and tolerances of the tubing shall be as specified in table 1 or 2 when the tubing is measured in accordance with 4.3 . wire gage 19 1 Later issues of the ASTM publications referenced in this ...
Page 4
Low temperature flexibility — The tubing shall remain flexible and free from cracks when tested in accordance with 4.10 . 3.11 . Minimum proof pressure ( applicable only ... This can be determined after completion of the heating cycle ...
Low temperature flexibility — The tubing shall remain flexible and free from cracks when tested in accordance with 4.10 . 3.11 . Minimum proof pressure ( applicable only ... This can be determined after completion of the heating cycle ...
Page 5
Inside diameter — The inside diameter shall be determined in accordance with ASTM D 1675–65 , Standard Methods of Testing Electrical Grade Polytetrafluoroethylene Tubing.3 4.3.2 . Wall thickness The wall thickness shall be determined in ...
Inside diameter — The inside diameter shall be determined in accordance with ASTM D 1675–65 , Standard Methods of Testing Electrical Grade Polytetrafluoroethylene Tubing.3 4.3.2 . Wall thickness The wall thickness shall be determined in ...
Page 6
Weight loss — The loss in weight shall be determined in accordance with ASTM D 1675–65 , except that the minimum weight of the test specimens shall be 50 grams , and the specimens shall be heated in a forced - draft oven for 3 hours at ...
Weight loss — The loss in weight shall be determined in accordance with ASTM D 1675–65 , except that the minimum weight of the test specimens shall be 50 grams , and the specimens shall be heated in a forced - draft oven for 3 hours at ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Common terms and phrases
acceptance ACCEPTORS accordance with ASTM acts American applicable Association ASTM D basis Bureau of Standards Calif Center Chemical Chicago Class committee Company complete compliance conditioned conforming consists Corporation Department of Commerce determined determined in accordance Development distributors divisions document electrical Engineering Standards Services established Fluorocarbon Government Grade Inch Inch Inch inclusive indicated industry inside diameter Institute intended interested less listed longitudinal mandrel Mass Materials maximum measurement Melting methods of test MICHIGAN Minimum proof pressure minus National Bureau Office of Engineering Ohio percent Philadelphia physical Pittsburgh plastic tubing points Polytetrafluoroethylene PTFE Procedures Processing Prod Programs promotes proposed provides PTFE tubing published purchaser Reference Representing requirements Research Road Rubber specified in table Stand statement strength and elongation technical Technology temperature tensile strength tested in accordance Type UNITED users Voluntary Product Standard wall thicknesses Washington weight
Bibliographic information
| Title | NBS Voluntary Product Standard |
| Author | United States. National Bureau of Standards |
| Contributor | United States. Dept. of Commerce |
| Publisher | U.S. Department of Commerce, National Bureau of Standards, 1972 |
| Original from | the University of Michigan |
| Digitized | 18 Apr 2006 |
| Export Citation | BiBTeX EndNote RefMan |